Kiilto Masa adhesive and sealant 290 ml white
Request login credentials
Kiilto Masa adhesive and sealant is a versatile adhesive and sealing compound for construction as well as the shipbuilding, boating, and transport equipment industries. A 1-component adhesive compound for bonding and sealing moldings, building boards, metals, fiberglass, and various types of plastics. In wet rooms, for sealing pipe penetrations and floor drain connections; outdoors, for example, sealing roof penetrations and window flashings. Offers excellent weather and UV resistance, with good chemical resistance. Can be painted over. Solvent-free, also suitable for movement joints exposed to mechanical wear.
Benefits and features:- Good adhesion to many materials, excellent weather and UV resistance, available in several colors
- NSF registered: can be used in areas where food is handled
- For bonding and sealing
- Coverage for a 5 x 5 mm joint: approx. 12 m/cartridge
- Curing time 3 mm/day, approx. 10 mm/7 days
- For indoor and outdoor use
Applications:
The product adheres to various stone surfaces, concrete, most metals, wood, glass and glazed surfaces, as well as epoxy and polyester surfaces. With different plastic grades, an adhesion test should be carried out before actual use. Meets the M1 emissions classification for building materials. Solvent-free, contains no isocyanates or phthalates. Can be painted over with most water-based paints (always perform a paint test). Withstands weather exposure extremely well and has good UV light resistance. Good chemical resistance (diluted solutions). Resistant to seawater. Not suitable for glazing applications.
Certifications: M1, CE, IMO Wheelmark, NSF, LEED, Key Flag Symbol| Curing rate | 3 mm/day, approx. 10 mm/7 days (23 °C, 50 %RH) |
| Hardness | Shore A 40 |
| Shrinkage | approx. 2 % |
| Application temperature | +1 to +40 °C |
| Shear strength | 2.2 N/mm² (SS-SS) |
| Heat resistance, dry | -40 to +90 °C, +180 °C / 30 min |
| Maximum joint movement | ± 10 % |
| Tensile strength | 2.1 N/mm² (DIN 53504) |
| Elongation at break | 400 % (DIN 53504) |
| Coverage | 5 x 5 mm joint, approx. 12 m/cartridge |
| Density/specific gravity | approx. 1.59 kg/l |
| Type/binder | silyl-modified polymer |
| Storage | 18 months, unopened (+10–25 °C) |
| Viscosity | approx. 1.5 million mPas (BrookField H-Path T-F/2.5 +20 °C) |
| Skin formation time | approx. 15 min (23 °C, 50 %RH) |
| Form | high-viscosity paste |